Wire drawing |
| Description:
The wire-drawing bench is a low-speed laboratory facility. It
allows to draw wires from 15 mm down to 0.5 mm in successive passes.
The drawing dies are made of tungsten-carbide (with cobalt-binder).
Before each pass the wire is pointed with a swaging machine; it is
then inserted through the conical die and clamped to the drawhead.
Much attention should be paid to find the proper lubricant for each
wire material to be drawn.
|
| Technical details: | ||
| Robertson Pointing and wire drawing machine | ||
| Pointing Rolls | 9 | |
| Max. Diameter | 8 mm | |
| Wire drawing | ||
| Variable speed (Max.) Diameter op capstan Max.Diameter (annealed copper) Max. pulling force | 45.7 m/min 450 mm 9.5 mm 7.7 kN |
|
| K.U.Leuven wire drawing machine | ||
| Variable speed (Max.) Max. pulling force Max. Diameter (annealed copper) Option: Possibility to measure the pulling force by a load cell (Max.) | 0.8 m/min 9.8 kN 10 mm 9.8 kN |
|
| List of Dies (2a ~ 11°) | |||||
|---|---|---|---|---|---|
| Diameter | Reduction | Diameter | Reduction | Diameter | Reduction |
| 0.54 | 1.50 | 3.23 | |||
| 0.585 | 14.79 | 1.55 | 6.35 | 3.25 | 1.23 |
| 0.68 | 25.99 | 1.58 | 3.76 | 3.30 | 3.01 |
| 0.72 | 10.80 | 1.64 | 7.18 | 3.40 | 5.80 |
| 0.74 | 5.33 | 1.67 | 3.56 | 3.48 | 4.54 |
| 0.75 | 2.65 | 1.70 | 3.50 | 3.50 | 1.14 |
| 0.76 | 2.61 | 1.75 | 5.63 | 3.58 | 4.42 |
| 0.78 | 5.06 | 1.78 | 3.34 | 3.67 | 4.84 |
| 0.82 | 9.52 | 1.94 | 15.81 | 3.72 | 2.67 |
| 0.85 | 6.93 | 2.05 | 10.44 | 3.75 | 1.59 |
| 0.86 | 2.31 | 2.18 | 11.57 | 3.80 | 2.61 |
| 0.89 | 6.63 | 2.25 | 6.12 | 3.92 | 6.03 |
| 0.97 | 15.81 | 2.42 | 13.56 | 3.98 | 2.99 |
| 1.15 | 28.85 | 2.50 | 6.30 | 4.00 | 1 |
| 1.28 | 19.28 | 2.55 | 3.8 | 4.03 | 1.48 |
| 1.36 | 11.42 | 2.73 | 12.75 | 4.07 | 1.96 |
| 1.38 | 2.88 | 2.90 | 11.38 | 4.08 | 0.49 |
| 1.40 | 2.84 | 2.92 | 1.37 | 4.25 | 7.84 |
| 1.42 | 2.80 | 3.00 | 5.26 | 4.32 | 3.21 |
| 1.48 | 7.94 | 3.13 | 8.13 | 4.39 | 3.16 |
| 1.50 | 2.65 | 3.23 | 6.10 | 4.43 | 1.80 |
| List of Dies (continued) | ||||
|---|---|---|---|---|
| Diameter | Reduction | Diameter | Reduction | |
| 4.43 | 6.50 | |||
| 4.49 | 2.65 | 6.62 | 3.59 | |
| 4.55 | 2.62 | 7.20 | 15.46 | |
| 4.75 | 8.24 | 7.30 | 2.72 | |
| 4.78 | 1.25 | 7.46 | 4.24 | |
| 4.79 | 0.42 | 7.80 | 8.53 | |
| 4.85 | 2.46 | 8.46 | 14.99 | |
| 4.9 | 2.03 | 8.48 | 0.47 | |
| 5.06 | 6.22 | 9.22 | 15.41 | |
| 5.08 | 0.79 | 9.60 | 7.76 | |
| 5.10 | 0.78 | 10.00 | 7.84 | |
| 5.18 | 3.06 | 10.85 | 15.05 | |
| 5.34 | 5.90 | 11.50 | 10.98 | |
| 5.50 | 5.73 | 12.70 | 18.00 | |
| 5.61 | 3.88 | 13.80 | 15.31 | |
| 5.64 | 1.06 | 14.95 | 14.79 | |
| 5.74 | 3.45 |
|
||
| 5.95 | 6.93 | |||
| 6.10 | 4.86 | |||
| 6.15 | 1.62 | |||
| 6.50 | 10.48 | |||
| Room: H 00.25 |
| More Technical information: Techinfo@mtm.kuleuven.ac.be |
|
Copyright ©1999, Katholieke Universiteit Leuven Information provider: K.U.Leuven, Department MTM Page maintenance: Webmaster Comments on the contents: Webmaster Last modified: February, the 17th, 2000 |